MIL-DTL-53022 TY2


A two component, Epoxy Polyamide, corrosion inhibiting primer, suited for high performance application Lead and Chrome Free, outperforms Zinc Chromate primer

Caution :This product is for industrial use only.

Item #: MIL-DTL-53022
Rating: Not Rated Yet
Mil-Spec Number MIL-P-53022B
Color White
Volume Solids 56.1 %
Weight Solids 76.1 %
Theoretical Coverage @ 1 Mil Dry 760 ft²/gal
Viscosity 70 - 80 KU
Weight per Gallon 13.0
Gloss @ 60 Degree 10 - 30
VOC 3.1
Film Thickness 1.0 - 1.5 mils
Salt Spray Test 336 Hrs
Humidity Test 300 Hrs
Pencil Hardness 2H
Manufacturer Part Number N-1981A
Application Information
  • Methods: Conventional spray, HVLP, AAA, airless

  • Mix ratio: After thoroughly mixing, mix 4 parts comp. a with 1 part comp b, may be used with proportioning equipment- no induction (sweat) time required.

  • Reducer: Ideal reducer is T-236 Epoxy reducer, may use MIBK, MEK up to 15%

  • Cleaner: T-236 Epoxy reducer, or recommended cleaning solvent for this spec..

  • Pot life: 4-6 hours, 6-8 hours if reduced, at 70°F. Pot life diminishes as temp rises

  • Dry time: Air dry, set to touch 30 min. dry through 4 hrs., force dry 10 min flash- bake 30 min @ 180-200°F

  • Time to recoat: Time, temperature, film build as guides.

Surface Preparation

Surface should be clean of all grease, dirt, oil, rust and foreign material which would be detrimental to the coating

Safety Information

Consult the Material Safety Data Sheet prior to application for detailed information on the health and safety hazards.


This product must be stored in accordance with Local, State, and National Regulations.

Preferred storage conditions:

  • Keep containers in a dry space with adequate ventilation

  • The containers should be tightly sealed

  • Handle with care

  • Stir well before use

  • Shelf life is 12 months from date of manufacturing

Dry Time / Cure

Cure is a function of time, temperature, and film build coating is cured when the carrier solvent has evaporated. See time to recoat and dry time above.


Use of a mechanical mixer is highly recommended. This metal primer is very well suited for general industrial applications including heavy equipment, trailers and trucks.


The information is supplied as a guideline to our customers. The user must be aware of the cleaning, pretreatment, application and testing requirements for their specific job.